Synthesis of a Novel Flame Retardant Containing Phosphorus, Nitrogen, and Silicon and Its Application in Epoxy Resin

A novel flame retardant (TDA) containing phosphorus, nitrogen, and silicon was synthesized successfully via a controllable ring-opening addition reaction between 1,3,5-triglycidyl isocyanurate, 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, and 3-aminopropyltriethoxysilane, and TDA was then blended with diglycidyl ether of bisphenol A to prepare flame-retardant epoxy resins (EPs). The chemical structure and components of TDA were confirmed by Fourier transform infrared (FTIR) spectra, P-31 nuclear magnetic resonance, and X-ray photoelectron spectroscopy. Thermogravimetric analysis results indicated that after the introduction of TDA, cured EP maintained good thermal stability with a minimum initial decomposition temperature of 337.6 degrees C, and the char yields of a EP/TDA-5 sample significantly increased by 76.2% compared with that of the neat EP thermoset. Additionally, with the addition of 25.0 wt % TDA (1.05 wt % phosphorus loading), the limited oxygen index value of cured EP increased from 22.5% of pure EP to 33.4%, and vertical burning V-0 rating was easily achieved. Meanwhile, after the incorporation of TDA, the total heat release and total smoke production of the EP/TDA-5 sample obviously reduced by 28.9 and 27.7% in the cone calorimeter test, respectively. Flame-retardant performances and flame-retardant mechanisms were further analyzed by scanning electron microscopy, FTIR, energy-dispersive spectrometry, and pyrolysis gas chromatography/mass spectrometry. The results reveal that the synergistic effect of phosphorus, nitrogen, and silicon plays an excellent flame-retardant role in both gaseous and condensed phases. In addition, the mechanical and dynamic mechanical properties of cured EP thermosets are well maintained rather than destroyed. All the results demonstrate that TDA endows epoxy resin with excellent flame retardancy and possesses great promise in the industrial field.

Automated summary

A novel flame retardant containing phosphorus, nitrogen, and silicon was successfully synthesized and blended with epoxy resin to form a flame-retardant composite material with excellent thermal stability and flame retardancy. The composite material showed promising performance in industrial applications, demonstrating improved fire safety and reduced heat release compared to neat epoxy resin.