Microstructures and mechanical properties of 4 wt%TiB2/Al-Si-Cu-Zn (T6) composite thin-walled shell housing fabricated by high pressure die casting

The application demand of lightweight high-quality aluminum alloy parts in automotive and aerospace fields is increasingly. In aluminum matrix composites, reinforcing particles can significantly improve the performance of the matrix. In this paper, the microstructures and mechanical properties of die-cast 4 wt%TiB2/Al-9Si-3Cu-0.8Zn composite were systematically analyzed by x-ray diffraction, optical microscope, scanning electron microscopy, energy dispersive spectrometer, transmission electron microscopy and tensile testing. The composite was successfully fabricated from an Al-K2TiF6-KBF4 system by in situ melting technique. The research results show that the average grain sizes of the alpha-Al phase gradually decreased with the increase of filling distance. And the TiB2 particles were distributed around eutectic Si in irregular polyhedral morphology or nearly circular shape. Meanwhile, the crystal structures of Ti-B compound and long needle shaped nano-sized precipitated were identified and analyzed, and they were found to be TiB2 and Al2Cu phase, respectively. Tensile testing results show that the mechanical properties of die-cast composite clearly increase after T6 heat treatment. The yield strength, ultimate tensile strength and elongation could reach 311 MPa, 379 MPa and 2.8% respectively, with the best injection velocity (1.8 m s(-1)). The significantly enhancement of mechanical properties of composite after T6 heat treatment was mainly due to the introduction of TiB2 reinforcing phase and the precipitation of Al2Cu precipitate in the aging stage. The results implied that the introduction of TiB2 reinforced particles could improve the mechanical properties of die castings, which has an important guiding role for its practical application.

Automated summary

This paper systematically analyzed the microstructures and mechanical properties of die-cast 4 wt%TiB2/Al-9Si-3Cu-0.8Zn composite, and found that the introduction of TiB2 reinforcing phase significantly enhanced the mechanical properties, especially after T6 heat treatment.