Thin film metallic glass; Zero valent metals; Peroxymonosulfate activation; Dye degradation
Funding
- Applied Research Center for Thin-Film Metallic Glass from The Featured Areas Research Center Program within Ministry of Education (MOE) in Taiwan
Ask authors/readers for more resources
The study demonstrates the effective degradation of OG azo dye using Fe39Co39Si8B14 thin film metallic glasses (TFMGs) deposited on commercial filter paper, achieving a degradation rate of 98.6%. The amorphous structure of TFMG and the fibrous texture of the filter paper substrate contribute to the degradation efficiency. Additionally, TFMG-coated filter paper shows good reusability, suggesting a cost-effective and sustainable method for dye degradation.
In this work Fe39Co39Si8B14 thin film metallic glasses (TFMGs) of thickness ranged between 122- 475 nm were deposited by magnetron sputtering on a commercial filter paper to act as a peroxymonosulfate (PMS) activator for degradation of Orange G (OG) azo dye. Degradation of 98.6% was achieved in 16 min. The influence of parameters such as catalyst dosage, light irradiation intensity, dye and PMS concentration to the efficiency of degradation were also investigated. SEM and XPS results revealed that the outstanding performance was attributed to the abundance of amorphous zero valent metals given by the amorphous atomic packing structure of TFMG. Zero valent metals readily activated PMS and favored the generation of SO4 center dot- and center dot OH radicals, which were the responsible species in degrading OG dye molecules. Another contribution was from the fibrous and porous texture of the filter paper substrate which provides specific surface area as high as 1.152 m(2)/g. TFMG-coated filter paper also showed good reusability that repeated degradation was possible. Results suggests that applying TFMG on a textured substrate could drastically reduce the dosage of Fe-based metallic glass needed compared to its powder or foil counterparts, which is significantly more cost effective.