JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY
Volume 97, Issue 3, Pages 593-599Publisher
SPRINGER
DOI: 10.1007/s10971-021-05470-9
Keywords
Spinel ferrites; Activation energy; Dielectric loss; Particle size; Resistivity
Categories
Funding
- Research Centre of the Centre for Female Scientific and Medical Colleges, Deanship of Scientific Research, King Saud University
Ask authors/readers for more resources
By adjusting the chemical composition, the prepared ferrite samples with low dielectric loss and high resistivity suitable for microwave devices were achieved in this study.
The prepared ferrite system with chemical formula Mg0.6Li0.4YbxFe2-xO4; x = 0.00 and 0.1 having valuable magnetic and electrical properties. The X-ray diffraction data confirmed the cubic spinel structure with single phase. The one order increase in magnitude of dc resistivity was found with 'Yb' substitution as compared to Mg-Li based ferrites. The room temperature dielectric loss under the frequency of 3 GHz was 3 x 10(-3). By using better stoichiometric ratio, size and the nature of substituted element, one can achieve suitable combination of low dielectric loss and high resistivity. In present work, the dielectric study (as a function of frequency) was done in frequency range of 0.1-20 MHz at different temperatures. The magnetic properties were measured up to applied field of 2 KOe. The low values of dielectric loss and high value of dc resistivity suggested that prepared samples may be suitable for microwave devices. [GRAPHICS]