JOURNAL OF CLEANER PRODUCTION
Volume 290, Issue -, Pages -Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.jclepro.2020.125754
Keywords
Semi-dry flue gas desulfurization ash; Calcium sulfate whisker; Hydrothermal oxidation; Supersaturation
Categories
Funding
- National Natural Science Foundation of China [51704004]
- Anhui Natural Science Foundation [1808085QE133]
- Open fund of Key Laboratory of Metallurgical Emission Reduction & Resources Recycling (Anhui University of Technology), Ministry of Education [JKF19-08]
Ask authors/readers for more resources
The one-step preparation of calcium sulfate whiskers from flue gas desulfurization ash was successfully achieved using a hydrothermal method, with control of temperature, time, and speed parameters being crucial. Adding a medium solution purification link in the hydrothermal system contributes to the production of high-quality calcium sulfate whiskers products.
Calcium sulfate whiskers were prepared under hydrothermal conditions by a one-step method using semi-dry flue gas desulfurization ash with iron ore sintering as the raw material. The effects of temperature, time, speed, and other factors on the calcium sulfate whiskers morphology and growth rule were systematically studied in a high-pressure hydrothermal reaction system. The results demonstrate that the presence of calcium carbonate inhibits high-efficiency desulfurization ash oxidation at low temperatures and affects calcium sulfate whiskers growth. The calcium sulfite content in flue gas desulfurization ash increased to 81.17% when glacial acetic acid was used as the raw material for pickling. In the supersaturated hydrothermal system, the one-step preparation of calcium sulfate whiskers from flue gas desulfurization ash was successful at a reaction temperature of 140 degrees C, time of 30 min, initial pressure of 2 MPa, initial solid-liquid ratio of 1:30, and rotation speed of 300 r/min. A medium solution purification link was added to create calcium sulfate whiskers products in the hydrothermal reaction system. Calcium sulfate whiskers products with an average diameter of less than 0.8 mu m and average aspect ratio of over 140 were obtained at a purification temperature of 60 degrees C, purification agent concentration of 0.6 mmol/g, temperature of 140 degrees C, time of 30 min, and speed of 100 r/min. (C) 2021 Elsevier Ltd. All rights reserved.