Journal
JOURNAL OF MAGNESIUM AND ALLOYS
Volume 9, Issue 2, Pages 569-580Publisher
KEAI PUBLISHING LTD
DOI: 10.1016/j.jma.2020.02.022
Keywords
Mg-Li alloys; Recrystallization; Texture; Mechanical properties; Corrosion behavior
Categories
Funding
- National Natural Science Foundation of China [51901047]
- Start-up Foundation of Guangdong University of Technology [220413701]
- National College Students Innovation and Entrepreneurship Training Program [201911845185, xj201911845345]
Ask authors/readers for more resources
In this study, the microstructure, crystallographic texture, mechanical properties, and corrosion resistance of as-extruded HCP Mg-xLi (x = 1, 3, 5; in wt%) alloys were investigated. The results showed that the Mg-5Li alloy with high lithium content exhibited a low degree of dynamic recrystallization and strong prismatic texture, leading to higher mechanical strength along the extrusion direction. Additionally, the high lithium content improved the corrosion resistance of the alloy and mitigated groove-like corrosion.
The microstructure, crystallographic texture, mechanical properties and corrosion resistance of as-extruded HCP Mg-xLi (x = 1, 3, 5; in wt%) alloys were investigated. The results indicated that the HCP Mg-5Li alloy with high lithium content exhibited a low degree of dynamic recrystallization (DRX) compared with Mg-1Li and Mg-3Li alloys. Besides, the 45 degrees base (0001) texture of Mg-1Li alloy could turn into (11-20) and (10-10) prismatic texture of Mg-3Li and Mg-5Li alloys with c-axis approximately parallel to transverse direction (TD). As a result, the strong prismatic texture resulted in the mechanical anisotropy of as-extruded Mg-3Li and Mg-5Li alloys with higher mechanical strength and low elongation along extrusion direction (ED) (reverse for TD sample). Regarding of corrosion behaviors, filiform corrosion occurred in the three Mg-Li alloys, whilst the high lithium content could mitigate the groove-like corrosion and improve the corrosion resistance of Mg-5Li alloy, which was ascribed to the refined grains, prismatic texture and surface film. (C) 2020 Chongqing University. Publishing services provided by Elsevier B.V. on behalf of KeAi Communications Co. Ltd.