Facile fabrication of superhydrophobic paper with durability, chemical stability and self-cleaning by roll coating with modified nano-TiO2

A superhydrophobic paper with excellent robustness was fabricated by roll coating with modified nano-TiO2. First, nano-TiO(2)particles were hydrophobically modified by gamma-aminopropyltriethoxysilane and 1H, 1H, 2H, 2H-perfluorooctyltriethoxysilane (POTS). Then the paper coating composed of modified nano-TiO(2)particles as pigments and epoxy resin (EP) as adhesives was coated on a paper surface to create the desired surface morphology and surface energy. Compared with the uncoated filter paper, the prepared paper showed an improved rough surface morphology owing to the uniform layer of TiO(2)microclusters deposited on the fiber network. The superhydrophobic paper exhibited water contact angles (WCA) about 153 degrees +/- 1.5 degrees, and water sliding angles (WSA) about 3.5 degrees +/- 0.5 degrees, low surface adhesion and excellent bounce ability. The superhydrophobic paper can withstand a variety of wear and tear, such as tape stripping and knife scraping. The as-prepared superhydrophobic paper showed mechanical durability even after 20 wear cycles with sandpaper,thus sustaining excellent superhydrophobicity on the filter paper surface. Moreover, it remains fully functional even in environments with high concentrations of acid and alkali for 96 h. The superhydrophobicity was not affected after storage for 6 months in a natural environment. It was confirmed that the superhydrophobic paper surface exhibited excellent chemical stability, long-term stability and self-cleaning properties. The entire production process was operated under normal environment, without complex equipment; and, as such, has the possibility for large-scale production and application in industry.