Levulinic Acid Production from Delignified Rice Husk Waste over Manganese Catalysts: Heterogeneous Versus Homogeneous

Delignified rice husk waste (25.66% (wt) cellulose) was converted to levulinic acid using three types of manganese catalysts, i.e., the Mn3O4/hierarchical ZSM-5 zeolite and Mn3O4 heterogenous catalysts, as well as Mn(II) ion homogeneous counterpart. The hierarchical ZSM-5 zeolite was prepared using the double template method and modified with Mn3O4 through wet-impregnation method. The structure and physicochemical properties of the catalyst materials were determined using several solid-state characterization techniques. The reaction was conducted in a 200 mL-three neck-round bottom flask at 100 degrees C and 130 degrees C for a certain reaction time in the presence of 10% (v/v) phosphoric acid and 2% (v/v) H2O2 aqueous solution, and the product was analyzed using HPLC. In general, 5-hydroxymethyl furfural (5-HMF) as the intermediate product was produced after 2 h and decreased after 4 h reaction time. To conclude, the Mn3O4/hierarchical ZSM-5 heterogenous catalyst gave the highest yield (wt %) of levulinic acid (39.75% and 27.60%, respectively) as the main product, after 8 h reaction time.