Humic acid functionalized magnetic nanomaterials for remediation of dye wastewater under ultrasonication: Application in real water samples, recycling and reuse of nanosorbents

Water pollution by industrial sector is a great problem which hampers the sustainable development goals. Dye containing water effluent poses vast challenge to clean water before its discharge in to the surrounding ecosystem. Herein, we prepared humic acid functionalized Fe3O4 nanosorbents through an eco-friendly route and applied for decolorization of carcinogenic dye from water. The nanosorbents was characterized by AFM, BET surface area analyzer, FTIR, SEM-EDX, TEM, TGA/DTG, VSM and XRD. Adsorption experiments were conducted by taking the appropriate amount of dye in different sources of water under ultrasonication. Adsorption process was controlled by chemisorption in nature making pseudo-second-order model most suitable. Multilayer adsorption was taking place on the active sites of nanosorbents showing applicability of Freundlich isotherm model with highest adsorbed amount of 199.986 mg g(-1) at 323 K. Rise in temperature favors the remediation of colored effluent thus positive value of Delta H degrees (74.234 kJ mol(-1)) and negative value of Delta G degrees shows endothermic and spontaneous nature of adsorption system. Cationic surfactant CTAB favors the adsorption (<80%) while anionic SDS gives very low removal (>48%) because of the micelle formation at the surface of nanosorbents. Decolorization from real water samples shows that the adsorption of malachite green was 97, 90, 91, 87, and 86% for Ganga river water, tap water, well water, hand pump water and submersible water, respectively. The used Fe3O4/HA nanosorbents was easily recycled from water samples through 0.1 M HCl and nanosorbents was used up to five cycles with greater percentage of removal at 85%. (C) 2019 Elsevier Ltd. All rights reserved.