POLYMERS
Volume 12, Issue 3, Pages -Publisher
MDPI
DOI: 10.3390/polym12030515
Keywords
polybenzimidazole; fuel cell; proton exchange membrane; high temperature; hyperbranched cross-linker; imidazolium groups
Categories
Funding
- Natural Science Foundation of Guangdong Province [2015A030313546]
- Shenzhen Sci & Tech research grant [JCYJ20170818093417096]
- Shenzhen University [2018040]
Ask authors/readers for more resources
Highly phosphoric-acid (PA)-doped polybenzimidazole (PBI) membranes exhibit good proton conductivity at high temperatures; however, they suffer from reduced mechanical properties and loss of PA molecules due to the plasticity of PA and the weak interactions between PA and benzimidazoles, especially with the absorption of water. In this work, a series of PBIs with hyperbranched cross-linkers decorated with imidazolium groups (ImOPBI-x, where x is the weight ratio of the hyperbranched cross-linker) as high-temperature proton exchange membranes are designed and synthesized for the first time. We observe how the hyperbranched cross-linkers can endow the membranes with improved oxidative stability and acceptable mechanical performance, and imidazolium groups with strong basicity can stabilize the PA molecules by delocalization and hydrogen bond formation to endow the membranes with an enhanced proton conductivity and a decreased loss of PA molecules. We measured a high proton conductivity of the ImOPBI-x membranes, ranging from 0.058 to 0.089 S cm(-1) at 160 degrees C. In addition, all the ImOPBI-x membranes displayed good mechanical and oxidative properties. At 160 degrees C, a fuel cell based on the ImOPBI-5 membrane showed a power density of 638 mW cm(-2) and good durability under a hydrogen/oxygen atmosphere, indicating its promising use in anhydrous proton exchange membrane applications.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available