Effect of Magnesium Hydroxide and Aluminum Hydroxide on the Thermal Stability, Latent Heat and Flammability Properties of Paraffin/HDPE Phase Change Blends

In this study, paraffin was selected as the phase change material (PCM) and high-density polyethylene (HDPE) as the supporting material to prepare a flame-retardant PCM system. The system consisted of paraffin, HDPE, expanded graphite (EG), magnesium hydroxide (MH) and aluminum hydroxide (ATH). The thermal stability and flame retardancy were studied by thermo-gravimetric analysis (TGA), scanning electron microscopy (SEM) and cone calorimeter test (CONE). The SEM proved that the addition of MH and ATH can produce an oxide film on the surface of the composite material and form a physical barrier with the char layer, generated by the expansion of EG, preventing the transfer of heat and oxygen. The TGA test showed that, compared with other flame-retardant systems, the materials with added MH and ATH have a higher thermal stability and carbonization ability, and the amount of char residue has increased from 17.6% to 32.9%, which reduces the fire risk of the material. The flame retardant effect is obvious. In addition, the addition of MH and ATH has no significant effect on the phase transition temperature and latent heat value of PCMs. The CONE data further confirmed that MH and ATH can work with EG to prevent heat release, reduce the total heat release rate (THR) value and effectively suppress the generation of smoke, CO and CO2. The peak heat release rate (PHRR) value also decreased, from 1570.2 kW/m(2) to 655.9 kW/m(2).