Journal
THIN SOLID FILMS
Volume 692, Issue -, Pages -Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.tsf.2019.137598
Keywords
Titania; Nanotubes; Nitrogen doping; Thermal annealing; X-ray photoelectron spectroscopy; Diffuse reflectance spectroscopy; Band gap
Categories
Funding
- Ministry of Education, Science and Technological Development, Republic of Serbia [III 45019, III 45005]
- UEFISCDI [304/2011]
Ask authors/readers for more resources
The similar to 60 nm wide and similar to 2 mu m long TiO2 nanotubes were obtained by anodization of Ti films sputtered on F-doped tin oxide glass. For N-doping the samples were annealed in ammonia atmosphere. The effect of pre- and post-annealing in air on the nature and amount of incorporated N was studied by X-ray photoelectron spectroscopy. By measuring the absorption spectra of the obtained samples and interpreting the corresponding Tauc plots it was shown that the sample annealed just in ammonia showed the highest visible light absorption even after sputtering cleaning and a decrease of N amount from 3.8% to 1%. Pre and/or post annealing in air led to smaller amount of incorporated N, that caused less pronounced absorption enhancement and smaller band gap narrowing compared to the sample annealed only in ammonia. By fitting of N 1 s line, the contribution that was assigned to substitutional N was detected only in the samples that did not sustained post-annealing. The study showed that post-annealing in air might lead to partial conversion of N atoms in TiO2 to oxidized nitrogen species that are easily removed with sputtering. It is also possible that substitutional nitrogen was suppressed by oxygen from air to move to interstitial site. Weakly bonded NOx surface species, which are cleaned away by sputtering, can be removed by post-annealing in air. Those surface species could act as sensitizers and when their amounts are reduced, the core absorption properties, as a result of interstitial incorporation of N in TiO2 structure, were revealed. Much lower visible light sensitization was achieved in the case of pre-annealed sample in comparison to sample without pre-annealing, regardless the same quantity and type of incorporated nitrogen.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available