Journal
CERAMICS INTERNATIONAL
Volume 46, Issue 9, Pages 14269-14272Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2020.02.155
Keywords
Silicon carbide; Pressureless joining; Microstructure; Shear strength
Categories
Funding
- National Major Science and Technology Projects of China [2015ZX06004001]
- National Key R&D Program of China [2017YFB0702404]
- Shenzhen Clean Energy Research Institute, China
Ask authors/readers for more resources
Silicon carbide ceramics were pressureless joined by using Ti foil and Si powder, which generated Ti3SiC2 phase as the interlayer. The phase composition, microstructure and the shear strength were investigated. It was revealed that the SiC assembly after joining at 1500 degrees C showed the high shear strength of 76.2 +/- 19.5 MPa. The secondary phase of TiC within the interlayer was expected to contribute to densification improvement of Ti3SiC2 phase and thermal stress reduction.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available