MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
Volume 767, Issue -, Pages -Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.msea.2019.138434
Keywords
Austenitising; Austempered CGI; Ausferrite matrix; Retained austenite; Mechanical properties; EBSD
Categories
Funding
- Stiftelsen for kunskaps- och kompetensutveckling (KK-Foundation), Sweden under the ProSpekt scheme [GNR. 20170021]
Ask authors/readers for more resources
This study investigates the effect of austempering temperature and time on the microstructural and mechanical properties of unalloyed Compacted Graphite Iron (CGI) with an initially ferritic matrix structure. The as-cast CGI samples were first austenitised at 900 degrees C for 60 min in a furnace, then austempered in a closed salt bath at three austempering temperatures - 275, 325, and 375 degrees C - for different times; 30, 60, 90, and 120 min. Tensile properties, Brinell, Vickers and Rockwell C hardness values were evaluated for the as-cast and austempered CGI ones. LOM and SEM, EBSD analysis techniques were used for microstructure and phase analysis. A mixture of acicular ferrite and retained austenite was achieved in the austempered CGI samples. In general, a decrease in austempering temperature resulted in a decrease in retained austenite content, corresponding improvements in hardness and tensile strength, and a decrease in elongation values.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available