Thin carbon hollow fiber membrane with Knudsen diffusion for hydrogen/alkane separation: Effects of hollow fiber module design and gas flow mode

Recovery of heavier hydrocarbons, C-2-C-4 olefins and paraffins, from gas streams is of great importance economically. In this study, asymmetric carbon hollow fiber membranes (CHFMs) were prepared by a one-step vacuum-assisted dip coating and pyrolysis, and investigated for H-2/CO2 , H-2/C2H6, and H-2/C3H8 separations. To increase the mechanical strength of the CHFMs, a porous alumina hollow fiber with ID/OD = 2 mm/4 mm was used as the supporting material. A solution of polyetherimide in N-methyl-2-pyrrolidone was used as the casting solution. The effects of (1) membrane preparation parameters, (2) fiber packing densities, (3) fiber packing arrangement, and (4) gas flow configuration (inside-out or outside-in) on the gas-separation performance were also investigated. The results showed that decreasing the concentration of the casting dope and the number of coating cycles was found to be the most effective approach to increase the H-2 permeance, while maintaining the H-2/CO2 selectivity. Further, as the fiber packing density was increased from 5.54% to 38.78% for the hexagonal packing configuration, the H-2 permeance increased from 362.04 GPU to 711.61 GPU, without any decrease in the gas selectivity. The as-prepared CHFM exhibited the maximum gas permeance of 711.61 GPU for H-2 and the following gas selectivity: 2.79, 4.65, and 5.34 towards H-2/CO2, H-2/C2H6, and H-2/C3H8, respectively. The successful preparation and modularization of the CHFM is advantageous and industrially relevant for several gas-separation applications, such as H-2 energy production from CO2, C2H6, and C3H8 and olefins/paraffins recovery. (C) 2019 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.