Journal
POLYMER DEGRADATION AND STABILITY
Volume 167, Issue -, Pages 1-9Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.polymdegradstab.2019.06.012
Keywords
Residual chlorine; Accelerated degradation test; Polybutylene; Water pressure
Categories
Ask authors/readers for more resources
In this paper, we report a novel technique that enabled us to easily and effectively conduct an accelerated degradation test on a small pressure vessel for potable and hot water pipes. Accelerated degradation tests were carried out on polybutene (PB) pipes with and without pressurization, under chlorinated and non-chlorinated water at 80 degrees C; the higher-order structure changes, residual antioxidant agents, and degradation characteristics of the PB pipes were evaluated. In the degradation test under chlorine water, the isothermal oxidation induction time (1-OIT) time and the mechanical properties decreased with increasing aging time. Additionally, micro-Fourier transform infrared spectroscopy (FT-IR) imaging revealed the distribution of antioxidants in the PB pipe before and after the test, while in the degradation test under pressure, the residual amount of antioxidants was smaller, and the chemiluminescence intensity was higher compared with the test that was not pressurized. These results strongly suggest that not only dissolved chlorine but also water pressure contribute to promoting the degradation of plastic pipes, and that the simple pressure vessels allow the safe and easy testing of accelerated degradation. (C) 2019 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available