JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
Volume 40, Issue 2, Pages 267-275Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2019.09.030
Keywords
SiC; CaO-Al2O3-SiO2 glass; Bonding; Microstructure; Shear strength
Categories
Funding
- National Natural Science Foundation of China [51775142, 51805113]
- China Postdoctoral Science Foundation [2018M631923]
- Fundamental Research Funds for the Central Universities [HIT.NSRIF.2019006]
Ask authors/readers for more resources
CaO-Al2O3-SiO2 (CAS) glass ceramics were designed and prepared using a melt-quench approach. The coefficient of the thermal expansion (CTE) of the synthesized CAS (4.12 x 10(-6) K-1) matched perfectly with that of the SiC ceramic (4.01 x 10(-6) K-1). Thermal analysis of the CAS was conducted. Then the joining of the SiC ceramics by the CAS glass ceramics under various process parameters were conducted. The bonding temperature affects the fluidity of the CAS glass and the oxidation of the SiC substrate. The holding duration decides the infiltration of the CAS glass into the SiC substrate. The optimal bonding parameter is 1400 degrees C/10 min and the corresponding highest shear strength of the SiC/CAS/SiC bonded joints in average was 56 MPa. Fracture observation was also conducted to help analyze the relationship between the interfacial microstructure and the joint strength. Finally, the formation mechanism of the SiC/CAS/SiC bonded joints was proposed.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available