Journal
JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME
Volume 142, Issue 1, Pages -Publisher
ASME
DOI: 10.1115/1.4044440
Keywords
Zn-22Al alloy; ultra-fine grain; micro deep drawing; formability
Funding
- Karadeniz Technical University [BAP03-1218, 10.13039/501100004045]
Ask authors/readers for more resources
This study aimed to investigate the micro deep drawability of the Zn-22Al alloy at room temperature in which it shows superplastic properties. To this goal, first the two-step equal channel angular extrusion (ECAE) process was carried out to obtain an ultra-finegrained structure (UFG). Upon achieving the grain size of 200 nm, the formability of the alloy at room temperature and at a high strain rate was investigated both experimentally and numerically. Micro deep drawing experiments were performed at different deep drawing ratios (1.66, 1.84, 2.0, and 2.25) and for different sheet thicknesses (0.2, 0.4, and 0.6 mm). The finite element model of the micro deep drawing was also established to assess and compare the thickness variation in deep drawn parts. Results showed that the superplastic Zn-22Al alloy has a great potential in microforming applications. It was also noted that the limiting drawing ratio can be obtained as high as 2.25 in the room temperature condition.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available