Journal
JOURNAL OF ALLOYS AND COMPOUNDS
Volume 801, Issue -, Pages 558-567Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2019.05.349
Keywords
Ruddlesden-Popper phase; Nd2NiO4; Ca-doping; High-temperature behavior; Oxygen electrode; Ceramic membrane
Categories
Funding
- Government of the Russian Federation [02.A03.21.0006]
Ask authors/readers for more resources
Layered lanthanide nickelates of the first order with a K2NiF4-type structure, including Nd2NiO4, are considered as prospective oxygen electrode materials for different high-temperature electrochemical devices, membrane materials and catalysts. The presence of highly-mobile over-stoichiometric oxygen in their structure, the content of which depends on the synthesis and ambient conditions, strongly influences their functional properties. In this study, the materials of the Nd2-xCaxNiO4+delta (x = 0-1.0) series were obtained via a citrate-nitrate method. The Ca substitution limit was found to be equal to 30 mol %. The high-temperature structural, thermo-mechanical and electrical properties of the materials obtained were investigated in close relation with their oxygen over-stoichiometry. It was found that the absolute oxygen content decreased with Ca doping, which resulted in a transition from an orthorhombic structure (Fmmm sp. gr.) at x = 0, 0.1 to a tetragonal structure (I4/mmm sp. gr.) at x = 0.2, 0.3 and then, with further increase in Ca doping, to an orthorhombic structure (Bmab sp. gr.). Dilatometric curves for all the samples possessed high-temperature breaks corresponding to the structural changes caused by oxygen release upon heating, which was revealed in the HT-XRD and TGA-DSC experiments. There was a tendency for the thermal expansion coefficient to decrease both in the low and high temperature range with Ca doping. The minimum average TEC values were found for the samples with x = 0.4 (12.1 x 10(-6) K-1) and with x = 0.6 (11.8 x 10(-6) K-1) according to the HT-XRD and dilatometry data, respectively. There was a maximum at x = 0.4 (135 S cm(-1)) on the concentration dependence of the total conductivity obtained in the dc four-probe measurements. Materials with a medium Ca content (0.3-0.4), possessing moderate CTE values (similar to 12 x 10(-6) K-1), close to those of the majority of solid-state electrolytes, and showing a high level of total conductivity, can be recommended as promising materials for various electrochemical applications. (C) 2019 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available