Journal
ELECTROCHIMICA ACTA
Volume 314, Issue -, Pages 81-88Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2019.05.082
Keywords
3D printing; Li4Ti5O12; Low temperature direct writing; Lithium-ion battery
Categories
Funding
- National Natural Science Foundation of China [51705334, 51603125]
- Natural Science Foundation of Guangdong Province, China [2016A030310030]
- Shenzhen SciTech Project [JCYJ20180305125025855]
Ask authors/readers for more resources
3D printing has the capability of fabricating highly complex three-dimensional (3D) objects with tailored shapes and geometries, thereby offering an unparalleled tool for the creation of unconventional electrodes for lithium-ion batteries. In this study, high mass loading ultrathick porous Li4Ti5O12 (LTO) electrodes were fabricated via low temperature direct writing for the first time. A LTO ink that was capable of freezing at low temperature was developed and the 3D printing process was optimized to obtain the optimal printing parameters. LTO electrodes with the thickness of similar to 200 mu m, similar to 450 mu m and similar to 820 mu m and the corresponding mass loading of similar to 13.3 mg cm(-2), 24.1 mg cm(-2) and 32.3 mg cm(-2) were fabricated. These thick LTO electrodes displayed impressive areal capacities up to similar to 4.8 mAh cm(-2) @ 0.2 C and similar to 3.6 mAh cm(-2) @ 2.0 C with the electrode thickness of 820 mu m. All the thick electrodes showed excellent rate capacities below the charge/discharge rate of 2.0 C and excellent cycling performance with no deterioration in specific capacities after 100 cycles at 0.5 C. Cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) revealed that the thick LTO electrodes had excellent reversibility and good kinetics of electrochemical reactions. The major defect of the thick LTO electrodes is the degradation of rate capacities at high charge/discharge rate up to 5.0 C due to the slow kinetics resulted from large thickness. (C) 2019 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available