Journal
MATERIALS RESEARCH EXPRESS
Volume 6, Issue 9, Pages -Publisher
IOP PUBLISHING LTD
DOI: 10.1088/2053-1591/ab2de6
Keywords
forming limit diagram; anisotropy; SEM; microstructure; mechanical properties; Mg-7Li-1Zn alloys
Categories
Funding
- Iran National Science Foundation (INSF)
Ask authors/readers for more resources
In this article, the mechanical properties, microstructure, forming limit diagram (FLD) and anisotropy of dual phase Mg-7Li-1Zn alloy have been evaluated by a uniaxial tensile test at three directions, scanning electron microscopy (SEM), optical microscopy (OM) and hemispherical punch test at ambient temperature. The optical microscopy images showed that the microstructure of as-cast LZ71 alloy possesses a dual phase microstructure such as beta-Li matrix with body-centered cubic (BCC) structure and a partitioned alpha-Mg phase with hexagonal closest packed (HCP) structure in lath shape. After rolling process, the alpha-Mg phase has been elongated and arranged in the rolling direction and anisotropy at different directions increased, but after full annealing, microstructure arranged more uniform and changed from elongated to the uniform structure which this is the factor that reflects the reduction of anisotropy. FLD shows the limiting surface strains that sheet metal can endure before the start of localized necking and fracture at different deformation modes in tension-tension and tension-compression loading paths. The FLD of Mg-7Li-1Zn showed that this material has desirable formability due to the BCC structure with high slip system in the ambient temperature. Also, the results of the tensile test matched with the obtained FLD. Results of SEM revealed many dimples and some flat and cleavage planes. They showed the combination of ductile and brittle fracture, but the ductile fracture is the dominant fracture mechanisms for Mg-7Li-1Zn. In summary, in the dual phase, Mg-Li alloys via controlling the weight percent of lithium and other alloying elements can be achieved the desired mechanical properties and used for various applications.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available