APPLIED SURFACE SCIENCE
Volume 378, Issue -, Pages 224-230Publisher
ELSEVIER
DOI: 10.1016/j.apsusc.2016.03.181
Keywords
Ni-super alloys; Hot corrosion; Oxidation
Ask authors/readers for more resources
Superalloys are extensively used at high temperature applications due to their good oxidation and corrosion resistance properties in addition to their high stability were made at high temperature. Experimental measurements of hot corrosion at high temperature of Inconel 617 and Inconel 738 superalloys. The experiments were carried out at temperatures 700 degrees C, 800 degrees C and 900 degrees C for different exposure times to up to 100 h. The corrosive media was NaCl and Na2SO4 sprayed on the specimens. Seven different specimens were used at each temperature. The corrosion process is endothermic and the spontaneity increased by increasing temperature. The activation energy was found to be Ea = 23.54 and E-a = 25.18 Kj/mol for Inconel 738 and Inconel 617 respectively. X-ray diffraction technique (XRD) was used to analyze the formed scale. The morphology of the specimen and scale were examined by scanning electron microscopy (SEM). The results show that the major corrosion products formed were NiCr2O4, and Co Cr2O4 spinles, in addition to Cr2O3. (C) 2016 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available