APPLIED PHYSICS LETTERS
Volume 109, Issue 9, Pages -Publisher
AMER INST PHYSICS
DOI: 10.1063/1.4962125
Keywords
-
Categories
Funding
- Australian Research Council (ARC) [DP120103968, DP130100415]
- Danish Independent Research Council\Technology and Production Sciences [12-127449]
Ask authors/readers for more resources
The electro-mechanical coupling mechanisms in polycrystalline ferroelectric materials, including a soft PbZrxTi1-xO3 (PZT) and lead-free 0.9375(Bi1/2Na1/2)TiO3-0.0625BaTiO(3) (BNT-6.25BT), have been studied using a surface sensitive low-energy (12.4 keV) and bulk sensitive high-energy (73 keV) synchrotron X-ray diffraction with in situ electric fields. The results show that for tetragonal PZT at a maximum electric field of 2.8 kV/mm, the electric-field-induced lattice strain (epsilon(111)) is 20% higher at the surface than in the bulk, and non-180 degrees ferroelectric domain texture (as indicated by the intensity ratio I-002/I-200) is 16% higher at the surface. In the case of BNT-6.25BT, which is pseudo-cubic up to fields of 2 kV/mm, lattice strains, e111 and epsilon(200), are 15% and 20% higher at the surface, while in the mixed tetragonal and rhombohedral phases at 5 kV/mm, the domain texture indicated by the intensity ratio, I-111=I-11 (1) over bar and I-002/I-200, are 12% and 10% higher at the surface than in the bulk, respectively. The observed difference in the strain contributions between the surface and bulk is suggested to result from the fact that surface grains are not constrained in three dimensions, and consequently, domain reorientation and lattice expansion in surface grains are promoted. It is suggested that the magnitude of property difference between the surface and bulk is higher for the PZT than for BNT-6.25BT due to the level of anisotropy in the strain mechanism. The comparison of the results from different methods demonstrates that the intergranular constraints have a significant influence on the electric-field-induced electro-mechanical responses in polycrystalline ferroelectrics. These results have implications for the design of higher performance polycrystalline piezoelectrics. Published by AIP Publishing.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available