Journal
APPLIED GEOCHEMISTRY
Volume 71, Issue -, Pages 110-122Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.apgeochem.2016.06.003
Keywords
Ce sequestration; Oxidation; Cerianite; CeO2; Biogenic manganese oxide; Mn(II)-oxidizing fungi
Categories
Funding
- Japan Society for the Promotion of Science KAKENHI [25340094, 16K00615]
- Environmental Research and Technology Development Fund, Ministry of the Environment [3K133012]
- Grants-in-Aid for Scientific Research [16K00615] Funding Source: KAKEN
Ask authors/readers for more resources
Sequestration of Ce3+ by biogenic manganese oxides (BMOs) formed by a Mn(II)-oxidizing fungus, Acremonium strictum strain KR21-2, was examined at pH 6.0. In anaerobic Ce3+ solution, newly formed BMOs exhibited stoichiometric Ce3+ oxidation, where the molar ratio of Ce3+ sequestered (Ceseq) relative to Mn2+ released (Mnrel) was maintained at approximately two throughout the reaction. A similar Ce3+ sequestration trend was observed in anaerobic treatment of BMOs in which the associated Mn(II) oxidase was completely inactivated by heating at 85 degrees C for 1 h or by adding 50 mM NaN3. Aerobic Ce3+ treatment of newly formed BMO (enzymatically active) resulted in excessive Ce3+ sequestration over Mn2+ release, yielding Ce-seq/Mn-rel > 200, whereas heated or poisoned BMOs released a significant amount of Mn2+ with lower Ce3+ sequestration efficiency. Consequently, self-regeneration by the Mn(II) oxidase in newly formed BMO effectively suppressed Mn2+ release and enhanced oxidative Ce3+ sequestration under aerobic conditions. Repeated treatments of heated or poisoned BMOs under aerobic conditions confirmed that oxidative Ce3+ sequestration continued even after most Mn oxide was released from the solid phase, indicating auto-catalytic Ce3+ oxidation at the solid phase produced through primary Ce3+ oxidation by BMO. From X-ray diffraction analysis, the resultant solid phases formed through Ce3+ oxidation by BMO under both aerobic and anaerobic conditions consisted of cerianite with crystal sizes of 5.00-7.23 angstrom. Such nano-sized CeO2 (CeO2, BMO) showed faster auto-catalytic Ce3+ oxidation than that on well-crystalized cerianite under aerobic conditions, where the normalized pseudo-first order rate constants for auto-catalytic Ce3+ oxidation on CeO2, BMO was two orders of magnitude higher. Consequently, we concluded that Ce3+ contact with BMOs sequesters Ce3+ through two oxidation paths: primary Ce3+ oxidation by BMOs produces nano-sized crystalline cerianite, and subsequent auto-catalytic Ce3+ oxidation efficiently occurs using dissolved oxygen as the oxidizing agent. Pretreatment of newly formed BMOs with La3+ solution resulted in decreased rate constants for primary Ce3+ oxidation by BMO due to site blocking by La3+ sorption. The results presented herein increase our understanding of the role of BMO in oxidative Ce3+ sequestration process(es) through enzymatic and abiotic paths in natural environments and provide supporting evidence for the potential application of BMOs towards the recovery of Ce3+ from contaminated waters. (C) 2016 Elsevier Ltd. All rights reserved.