Journal
MATERIALS
Volume 12, Issue 10, Pages -Publisher
MDPI
DOI: 10.3390/ma12101577
Keywords
titanates; morphology; molten salt; crystal growth; Formation
Categories
Funding
- Natural Science Foundation of China [51425202, 51772150]
- Natural Science Foundation of Jiangsu Province [BK20160093]
- Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD)
Ask authors/readers for more resources
Titanates materials have attracted considerable interest due to their unusual functional and structural properties for many applications such as high-performance composites, devices, etc. Thus, the development of a large-scale synthesis method for preparing high-quality titanates at a low cost is desired. In this study, a series of quaternary titanates including K0.8Mg0.4Ti1.6O4, Na0.9Mg0.45Ti1.55O4, Na0.75Fe0.75Ti0.25O2, NaFeTiO4, and K2.3Fe2.3Ti5.7O16 are synthesized by a simple molten salt method using inexpensive salts of KCl and NaCl. The starting materials, intermediate products, final products, and their transformations were studied by using TG-DSC, XRD, SEM, and EDS. The results show that the grain size, morphology, and chemical composition of the synthesized quaternary titanates can be controlled simply by varying the experimental conditions. The molar ratio of mixed molten salts is critical to the morphology of products. When KCl:NaCl = 3:1, the morphology of K0.8Mg0.4Ti1.6O4 changes from platelet to board and then bar-like by increasing the molar ratio of molten salt (KCl-NaCl) to raw materials from 0.7 to 2.5. NaFeTiO4 needles and Na0.75Fe0.75Ti0.25O2 platelets are obtained when the molar ratio of molten salt (NaCl) to raw materials is 4. Pure phase of Na0.9Mg0.45Ti1.55O4 and K2.3Fe2.3Ti5.7O16 are also observed. The formation and growth mechanisms of both potassium magnesium titanates and sodium iron titanates are discussed based on the characterization results.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available