Amorphous thin film; Wear; Corrosion; Tribocorrosion; Coefficient of friction; Oxide film
Funding
- US National Science Foundation [DMR-1455108]
Ask authors/readers for more resources
Amorphous metallic thin films show great promise for applications where mechanical and chemical attack co-exist due to their excellent wear, corrosion, and tribocorrosion resistance. In this research, the effect of scratching frequency on amorphous Al-Mn thin film were studied in simulated seawater by varying the scratching frequency from 0.05 to 1 Hz in reciprocal motion. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were applied to characterize the microstructure before and after tribocorrosion testing. Post-tribocorrosion topography measurement was performed using non-contact optical 3D profilometer. It was found that the total tribocorrosion rate, including both mechanical and chemical wear, increased with increasing scratching frequency. Mechanical wear increased with scratching frequency, mostly related to an increment of coefficient of friction and real contact area. On the other hand, chemical wear tend to increase with scratching frequency, most likely due to faster repassivation kinetics at lower frequency. Cross-sectional TEM analysis shows that the disordered surface layer primarily consists of aluminum oxide where manganese is completely absent.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available