Journal
BIOMACROMOLECULES
Volume 16, Issue 3, Pages 1021-1031Publisher
AMER CHEMICAL SOC
DOI: 10.1021/acs.biomac.5b00014
Keywords
-
Funding
- National Science Foundation Partnerships for International Research and Education (PIRE) Program [1243313]
Ask authors/readers for more resources
A series of biobased epoxy monomers were prepared from diphenolic acid (DPA) by transforming the free acid into n-alkyl esters and the phenolic hydroxyl groups into diglycidyl ethers. NMR experiments confirmed that the diglycidyl ethers of diphenolates (DGEDP) with methyl and ethyl esters have 6 and 3 mol % of glycidyl ester. Increasing the chain length of DGEDP n-alkyl esters from methyl to n-pentyl resulted in large decreases in epoxy resin viscosity (700-to-11 Pa.s). Storage modulus of DPA epoxy resins, cured with isophorone diamine, also varied with n-alkyl ester chain length (e.g., 3300 and 2100 MPa for the methyl and n-pentyl esters). The alpha transition temperature of the cured materials showed a linear decrease from 158 to 86 degrees C as the ester length increases. The Youngs modulus and tensile strengths were about 1150 and 40 MPa, respectively, for all the cured resins tested (including DGEBA) and varied little as a function of ester length. Degree of cure for the different epoxy resins, determined by FTIR and DSC, closely approached the theoretical maximum. The result of this work demonstrates that diglycidyl ethers of n-alkyl diphenolates represent a new family of biobased liquid epoxy resins that, when cured, have similar properties to those from DGEBA.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available