Journal
JOURNAL OF THE TAIWAN INSTITUTE OF CHEMICAL ENGINEERS
Volume 97, Issue -, Pages 480-488Publisher
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jtice.2019.02.019
Keywords
Activated carbon monolith; Lignin; Biomass waste; Binderless; Phosphoric acid
Categories
Funding
- Spanish Ministry of Economy and Competitiveness [CTQ2015-68654-R]
Ask authors/readers for more resources
The valorization of lignocellulosic biomass waste into bio-based materials is proposed in this work in order to obtain low-cost materials and to reduce environmental impacts. Cylindrical activated carbon monoliths (ACMs) were prepared from Alcell (R), Kraft lignin and olive stone by chemical activation with H3PO4. To our best knowledge, there is no previous information about the preparation of ACMs from any type of lignin. In this sense, the development of value-added lignin-based products could be crucial to the economic success of the bio-ethanol production within a biorefinery context. The extrusion of the adequate mixing, without any kind of binder, was carried out in an extruder designed by ourselves with different dies. Carbon monoliths without and with holes (25 or 120 channels/cm(2)) were obtained. In case of lignin precursors, a stabilization step was optimized to minimize the problems of plasticity and swelling of lignin. N-2 adsorption-desorption at -196 degrees C and Hg porosimetry results show that activated carbon monoliths presented pore size distributions in the micro and mesopore range, with high surfaces areas (c.a. 1500 m(2)/g) and relatively high mesopore volume (0.35 cm(3)/g). The bulk density of the monoliths is also very high (similar to 1.1 g/cm(3) for ACM from Alcell lignin), with compressive strength of 7.6 MPa. Electrochemical characterization of binderless activated carbon monolith electrodes was carried out by cyclic voltammetry and galvanostatic charge-discharge techniques. The ACM from olive stones presents the highest specific capacitance, with approximately 217 F/g and 205 F/cm(3). (C) 2019 Taiwan Institute of Chemical Engineers. Published by Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available