Polyurethane elastomers; Chain extender; Structural polymer; Thermal analysis
Funding
- University of Miskolc (ME) [EFOP-3.6.1-16-2016-00011]
- European Union
- European Social Fund
- BorsodChem Zrt. Company
Ask authors/readers for more resources
Polyurethane elastomers (PUR) based on polypropylene glycol and 4,4 '-diphenylmethane diisocyanate were prepared with various monoethylene glycol (mEG) contents. The aim of this study is to find a reliable polymer matrix for composites of improved thermal conductivity and testing fully in order to collect knowledge about its structure. Thermal conductivity was improved from 0.255 to 0.329 W m(-1) K-1 when increasing chain extender content. This attributed to a high appearance crystalline ordering level when adding high mEG content. Differential scanning calorimetry revealed a low transition temperature of soft segment at the same temperature around - 64 degrees C, due to constant polyol content. The enthalpy of melting increases with increasing mEG content. This is due to the increasing crystalline phase and hard segment phase separation within the PUR structure. Dynamic mechanical analysis results show the glass transition temperature of soft segment in the same temperature range between - 57 and - 52 degrees C and intensity peak of tan delta tends to decrease when mEG content was increased. On the other hand, the glass transition temperature of hard segment tends to increase from 10 to 93 degrees C and has high intensity peak of tan delta with increasing mEG content. Increasing the chain extender content can be enhancing the hard segment length in PUR structure and affecting both soft segment motion and hard segment motion. Increasing hard segment length might be obstructing soft segment motion and influence hard segment motion which is hard to move at low temperatures. Phase separation of soft and hard segment clearly observed using the DMA technique.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available