In situ construction of porous Ni/Co-MOF@Carbon cloth electrode with honeycomb-like structure for high-performance energy storage

Porous Ni/Co-organic framework with honeycomb-like structure was directly grown on the carbon cloth (Ni/Co-MOF@CC) through a hydrothermal process. The Ni/Co-MOF@CC displayed a high specific surface area with an average pore size of 3.05nm and excellent conductivity. The electrochemical performances of the porous Ni/Co-MOF@CC as the electrode of supercapacitors were evaluated using cyclic voltammetry, galvanostatic charge/discharge, and electrochemical impedance spectroscopy measurements in 2M KOH electrolyte. The Ni/Co-MOF@CC electrode exhibited a maximal specific capacity of 1180.5mCcm(-2) at 3mAcm(-2), good high-rate discharge ability (624.1mCcm(-2) at 60mAcm(-2)), and long-term cycling life (97.6% capacity retention after 5000 cycles). Our experiments demonstrated the practical application of mixed-MOFs as supercapacitors for next-generation energy storage devices.