Journal
ACTA MATERIALIA
Volume 112, Issue -, Pages 105-120Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.actamat.2016.03.051
Keywords
W/W-alloys; In-situ irradiations; TEM; Damage production; Microstructure evolution
Funding
- DOE Office of Nuclear Energy [DE-AC02-06CH11357]
- Culham Centre for Fusion Energy, St Edmund Hall, University of Oxford
- EPSRC [EP/H018921/1]
- Engineering and Physical Sciences Research Council [EP/H018921/1] Funding Source: researchfish
- EPSRC [EP/H018921/1] Funding Source: UKRI
Ask authors/readers for more resources
In-situ irradiations with 150 keV W+ ions have been performed on W and W-5wt.% (Re; Ta; V) alloys in a comprehensive study of the influences of irradiation temperature T-irr, dose, alloying elements and grain orientations on radiation damage production and microstructural evolution. For T-irr between 30 K and 1073 K, the first observable defects in pure W appeared at doses <= 0.01 dpa, and were most likely vacancy loops, with Burgers vectors predominantly of type b = 1/2 < 111 >. With increasing T-irr, the retained defect concentration decreased strongly and the maximum cluster size increased from similar to 1300 point defects at 30 K to similar to 2300 point defects at 1073 K. At all irradiation temperatures, the evolution of damage microstructures with dose from 0.1 to 1.0 dpa involved defect cluster migration, with mutual elastic interactions often leading to spatial inhomogeneities and loop reactions. In pure W, spatial ordering of loops was observed at doses >0.4 dpa and T-irr >= 773 K in grains close to z = < 001 >. No such ordering was found in similar grain orientations for the W-(Re; Ta) alloys, but it was found in the non-z = < 001 > grains. Post-irradiation analysis on W and W-5 wt% (Re; Ta) at 1.0 dpa showed that 1/2 < 111 > and < 100 > loops of both vacancy and interstitial type were present, at number densities similar to 10(15) loops m(-2). In all cases 1/2 < 111 > loops were dominant, the fraction of these with interstitial nature increased with T-irr, and the proportion of < 100 > loops decreased with increasing T-irr. Compared with pure W, microstructures in the W-(Re; Ta) alloys exhibited higher loop number densities and evolved more quickly with increasing dose towards damage saturation. (C) 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.