Journal
MATERIALS & DESIGN
Volume 86, Issue -, Pages 526-535Publisher
ELSEVIER SCI LTD
DOI: 10.1016/j.matdes.2015.07.113
Keywords
Magnesium alloys; Crystallographic texture; Twins; Torsion; Anisotropy; Mechanical properties
Categories
Funding
- National Science Foundation of China [51474241]
- National Key Basic Research Program of China [2013CB632204]
Ask authors/readers for more resources
We studied the effect of crystallographic orientation and temperature on the microstructure and mechanical properties of extruded A231 magnesium alloy bar by torsion and subsequent annealing. The results show that the orientation between torsion axis (TA) and extrusion direction (ED) has a significant impact on the microstructure evolution. With TA parallel to ED, profuse extension twins appeared. After annealing, zones close to the surface were completely recrystallized and refined, while the center still had some extension twins left. With TA perpendicular to ED, extension twins were inhibited. It is speculated that, except extension twins, contraction twins is also acting as a major deformation mode. Upon annealing, this specimen was completely recrystallized, even at the center, which is considered as a result of more preferred nucleation sites for static recrystallization from contraction twins. As demonstrated, the temperature has little impact on the microstructure development when twisted at room temperature or liquid nitrogen temperature. Moreover, the compression tests show that the compression ductility and yield strength were improved simultaneously for both samples when compressed on the direction either along ED or perpendicular to ED, due to the combined effects of grain refinement and texture weakening. (C) 2015 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available