Silica-based superhydrophobic coatings were produced on glass substrate by dip-coating process. Colloidal solutions containing nanoparticles of silica synthesized via seed growth method (single-and dual-sized particles) and dispersed in three different solvents, ethanol, silica sol and acidic silica sol, were used. Coatings with dual-sized particles in ethanol showed superhydrophobicity with a water contact angle of 155 degrees. The coating adhesion was improved with the use of acidic silica sol as solvent. Coatings prepared from colloidal solution containing 30 wt.% of dual-sized silica particles of 600 and 800 nm in acidic silica sol, showed hydrophilicity with water contact angle of 45 degrees before heat treatment due to the presence of -OH groups from acidic sol. After heat treatment at 250 degrees C for 2 h in atmospheric ambience, the -OH groups reacted to form cross-linked Si-O-Si resulting in superhydrophobicity of the coating with water contact angle of 147 degrees. In this work, silica based superhydrophobic coating was fabricated by adjusting the ratios of the dual-sized silica particles without carrying out any secondary step such as chemical modification or fluorination process on the coating.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available