Catalytic Activity of Mono- and Bi-Metallic Nanoparticles Synthesized via Microemulsions

Water-in-oil (w/o) microemulsions were used as a template for the synthesis of mono- and bi-metallic nanoparticles. For that purpose, w/o-microemulsions containing H2PtCl6, H2PtCl6 + Pb(NO3)(2) and H2PtCl6 + Bi(NO)(3), respectively, were mixed with a w/o-microemulsion containing the reducing agent, NaBH4. The results revealed that it is possible to synthesize Pt, PtPb and PtBi nanoparticles of similar to 3-8 nm in diameter at temperatures of about 30 degrees C. The catalytic properties of the bimetallic PtBi and PtPb nanoparticles were studied and compared with monometallic platinum nanoparticles. Firstly, the electrochemical oxidation of formic acid to carbon monoxide was investigated, and it was found that the resistance of the PtBi and PtPb nanoparticles against the catalyst-poisoning carbon monoxide was significantly higher compared to the Pt nanoparticles. Secondly, investigating the reduction of 4-nitrophenol to 4-aminophenol, we found that the bimetallic NPs are most active at 23 degrees C, while the order of the activity changes at higher temperatures, i.e., that the Pt nanoparticles are the most active ones at 36 and 49 degrees C. Furthermore, we observed a strong influence of the support, which was either a polymer or Al2O3. Thirdly, for the hydrogenation of allylbenzene to propylbenzene, the monometallic Pt NPs turned out to be the most active catalysts, followed by the PtPb and PtBi NPs. Comparing the two bimetallic nanoparticles, one sees that the PtPb NPs are significantly more active than the respective PtBi NPs.