The combinations of hollow MoS2 micro@nano-spheres: one-step synthesis, excellent photocatalytic and humidity sensing properties

The combinations of hollow MoS2 micro@nano-spheres were successfully fabricated through a one-step hydrothermal method. A possible growth mechanism was presented in detail based on time-dependent experimental facts. Besides, the photocatalytic activities of the samples were evaluated by monitoring the photodegradation of methylene blue (MB). The adsorption value of 150 mg g(-1) shows a strong adsorption capability in the dark. After irradiation for only 30 min, the remaining MB in solution is about 9.7%. Moreover, the humidity sensing properties of the samples were measured for the first time. The results revealed high sensitivity at high RH, small humidity hysteresis, fast response and recovery times, and good stability. The greatest sensitivity is 32.19 nF/% RH and the maximum hysteresis is similar to 6.3% RH. For humidity cycling of 17.2-89.5-17.2% RH, the response and recovery times are similar to 140 s and similar to 80 s, respectively. Capacitance fluctuations for one month are less than +/- 7% at various relative humidities (RHs).