JOURNAL OF MATERIALS CHEMISTRY A
Volume 1, Issue 33, Pages 9440-9448Publisher
ROYAL SOC CHEMISTRY
DOI: 10.1039/c3ta10501f
Keywords
-
Funding
- NSFC [51272004, U1203292]
Ask authors/readers for more resources
Hierarchical porous carbons (HPCs) for supercapacitors were synthesized from coal tar pitch using nano-sized gamma-Fe2O3 as a template and activation agent coupled with KOH activation by conventional and microwave heating. The HPCs were characterized by scanning electron microscopy, transmission electron microscopy, N-2 adsorption and X-ray diffraction techniques. The results show that the specific surface area (S-BET) of HPCs is tunable, and increases from 761 m(2) g(-1) to 1330 m(2) g(-1) as the mass ratio of gamma-Fe2O3 to the pitch increases in the mixture. The nano-sized gamma-Fe2O3 is reduced to Fe3O4, FeO, Fe in the activation reaction step. The carbon dioxide generated from the oxidation reactions of carbon monoxide via gamma-Fe2O3 reacts with carbon that is a kind of in situ physical activation, which results in the development of the porosity in HPCs. The large S-BET in HPCs are due to the synergistic effects including gamma-Fe2O3 template, KOH chemical activation, and physical activation resulting from the reactions of gamma-Fe2O3 and KOH activation. Under optimum conditions with the mass of coal tar pitch, gamma-Fe2O3, KOH at 4.2 g, 16.8 g and 6 g, the HPC made by conventional heating shows a high capacitance of 194 F g(-1) in 6 M KOH aqueous electrolyte and an energy density of 20.3 Wh kg(-1) in 1 M tetraethylammonia tetrafluoroborate in propylene carbonate electrolyte at a current density of 0.1 A g(-1). This work may pave a new way to produce high performance HPCs for energy storage devices.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available