ADVANCES IN MATERIALS SCIENCE AND ENGINEERING
Volume 2013, Issue -, Pages -Publisher
HINDAWI LTD
DOI: 10.1155/2013/629092
Keywords
-
Categories
Funding
- Research University Grant [05H22, Q.J130000.2509.05H22]
Ask authors/readers for more resources
Poly (lactic acid) (PLA)/chitosan (CS) natural polymer/epoxidised natural rubber (ENR) composites were successfully prepared through a solution casting method. The morphological characteristics of fabricated composites were investigated by scanning electron microscopy (SEM) and optical microscopy. The microstructure of PLA/ENR was significantly altered with the addition of CS. SEM analysis of composites fractured surfaces revealed smooth and homogeneous texture and good dispersion of CS. However for 15wt% CS composites, the phase segregation and poor adhesion between the polymers were observed. Fourier transform infrared spectroscopy revealed some levels of attractive interaction between CS, PLA, and ENR in the composites. The mechanical properties of composites in terms of tensile strength and tensile modulus were significantly improved with the addition of CS into the matrix while the percent elongation at break decreased. The tensile strength increased up to 5wt% CS loading for both PLA/CS and PLA/ENR/CS and thereafter decreased while Young's modulus increased up to 10wt%. However, when the CS content was increased to 15wt%, the tensile strength and tensile modulus were slightly decreased. These improvements were attributed to good dispersion of CS at the optimum filler levels and attractive interaction between the composites components.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available