Dielectric Relaxation Phenomena of Polylactic Acid with β-Crystalline Chitin

Journal

INTERNATIONAL JOURNAL OF POLYMER SCIENCE
Volume 2012, Issue -, Pages -

Publisher

HINDAWI LTD
DOI: 10.1155/2012/389491

Keywords

-

Funding

  1. Hachinohe Institute of Technology

Ask authors/readers for more resources

beta-crystalline chitin was added to polylactic acid (PLA), and this PLA was then heat-treated at 100 degrees C for one minute. The crystallinity of the heat-treated PLA increased to more than 40%, and its crystallization speed also increased significantly. The temperature dependency of these materials' relative permittivity (epsilon(r)') and relative dielectric loss factor (epsilon(r)'') was also examined. The dielectric absorption peak value in epsilon(r)'' curve of the PLA to which chitin was added and was smaller than that of PLA without chitin. Additionally, the Havriliak-Negami relaxation function was used to produce approximation curves for the frequency dependency of epsilon(r)' and epsilon(r)'' of chitin with PLA added at 80 degrees C. As a result, the relaxation strength (Delta epsilon) of the chitin with PLA added was smaller than that of the PLA without chitin, and the relaxation time (tau) of the chitin with PLA added was approximately 2.5 times larger than that of the PLA without chitin.

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.4
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available