In this work, we systematically investigated the structure-activity performance of nanosized Au/CeO2 and Au/Ce0.9Fe0.1O2-delta catalysts, along with nanocrystalline CeO2 (a)nd Ce0.9Fe0.1O2-delta supports, for the oxidation of carbon monoxide and benzylamine. An extensive physicochemical characterization was undertaken using XRD, BET surface area, BJH analysis, TG-DTA, XPS, TEM, Raman, AAS and CHN analyses. XRD studies confirmed the formation of smaller sized Ce0.9Fe0.1O2-delta nanocrystallites due to the incorporation of Fe3+ ions into the CeO2 lattice. Interestingly, Raman analysis revealed that the addition of Au remarkably improves the structural properties of the supports, evidenced by F-2g peak shift and peak broadening, a significant observation in the present work. TEM images revealed the formation of smaller Au particles for Au/Ce0.9Fe0.1O2-delta (similar to 3.6 nm) compared with Au/CeO2 (similar to 5.3 nm), attributed to ample oxygen vacancies present on the Ce0.9Fe0.1O2-delta surface. XPS studies indicated that Au and Fe are present in metallic and +3 oxidation states, respectively, whereas Ce is present in both +4 and +3 oxidation states (confirming its redox nature). Activity results showed that the incorporation of Fe outstandingly enhances the efficacy of the Au/CeO2 catalyst for both CO oxidation and benzylamine oxidation. A 50% CO conversion was achieved at similar to 349 and 330 K for Au/CeO2 and Au/Ce0.9Fe0.1O2-delta catalysts, respectively. As well, the Au/Ce0.9Fe0.1O2-delta catalyst showed similar to 99% benzylamine conversion with similar to 100% dibenzylimine selectivity for 7 h reaction time and 403 K temperature, whereas only 81% benzylamine conversion was achieved for the Au/CeO2 sample under similar conditions. The excellent performance of the Au/Ce0.9Fe0.1O2-delta catalyst is mainly due to the existence of smaller Au particles and an improved synergetic effect between the Au and the Ce0.9Fe0.1O2-delta support. It is confirmed that the oxidation efficiency of the Au catalysts is highly dependent on the preparation method.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available