Journal
WEAR
Volume 302, Issue 1-2, Pages 1583-1591Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.wear.2013.01.060
Keywords
Wind turbine; Gearbox; White etching area; Axial cracks; Fatigue; Bearing failure
Funding
- US Department of Energy's Wind and Water Power Program
- UChicago Argonne, LLC. [DE-ACO2-521 06CH11357]
Ask authors/readers for more resources
Renewable electricity generation from wind turbines presents unique challenges in reliability of their mechanical systems compared to utility-scale fossil fuelled generation. The number of turbines and their distribution make maintenance a difficult and infrequent task, and the peak loading events (caused by unsteady winds and grid faults) and harsh environmental conditions (temperature fluctuation and moisture) result in extreme operation. Consequently, wind turbine systems present one of the more challenging current practical tribological problems. Contact failures in gear and bearing components have been the source of costly repairs and downtime of the turbine's drivetrain and actuators. Gearboxes are commonly faced with abrasive wear, micropitting, scuffing, and macropitting issues, while the nacelle yaw and blade pitch mechanisms commonly suffer from false brinelling and fretting damage. This paper examines contact failures of bearings from wind turbine gearboxes. Scanning electron microscopy is used to observe the subsurface material microstructure. Areas of localized microstructural change, known as white etching area (WEA), are observed. Several theories as to the cause of the WEA are examined. Results of this analysis will help guide the development of lasting solutions to a pressing problem in wind turbines. (C) 2013 Published by Elsevier B.V.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available