Thick HS-PVD (Al,Cr)2O3 coatings for challenging cutting and die casting applications

In the last decades crystalline physical vapor deposition (PVD) Al2O3 coatings offered their great potential due to outstanding properties such as high hot hardness and wear resistance, especially concerning cutting applications. However, the properties of alumina strongly depend on the crystallographic phase. Thereby, the thermodynamically stable alpha-Al2O3 phase is the technical most interesting. The deposition of alpha-Al2O3 by chemical vapor deposition (CVD) is well-established, but requires high process temperatures, which reduce the selection of substrates. Another promising candidate concerning cutting and die casting applications is gamma-Al2O3. The formation of gamma-Al2O3 phase by PVD starts already at T >= 450 degrees C, allowing lower deposition temperatures. Regarding the wear protection of turning tools, a higher coating thickness (s >= 10 mu m) is beneficial. A possibility to deposit thick PVD alumina coatings is the high-speed PVD (HS-PVD) technology. In the present work thick, s >= 20 mu m, (Al, Cr)(2)O-3 films are deposited on cemented carbides at substrate temperatures T >= 500 degrees C, by means of HS-PVD. A metallic (Cr, Al) bond coat was employed to improve the adhesion of (Al, Cr)(2)O-3 coatings. In order to analyze the influence of the bond coat regarding the compound adhesion, scratch tests were conducted. For determining the coating morphology and thickness, scanning electron microscopy (SEM) was used. Phase analysis was carried out by X-ray diffraction spectroscopy (XRD). The mechanical properties were determined by means of nanoindentation. Regarding the use in high temperature applications, especially the formation of (Al, Cr)(2)O-3 at substrate temperatures of T approximate to 850 degrees C indicates that the use of the coatings is possible at equal high temperatures without phase transformation.