Keywords
HfO2; ALD; Cu; Resistive memory; XPS depth profile; TEM
Categories
Funding
- Air Force Research Laboratory award [FA87501110008]
Ask authors/readers for more resources
Hafnium oxide-based resistive memory devices have been fabricated on copper bottom electrodes. The HfOx active layers in these devices were deposited by atomic layer deposition (ALD) at 250 degrees C with tetrakis(dimethylamido) hafnium(IV) as the metal precursor and an O-2 plasma as the reactant. Depth profiles of the HfOx by X-ray photoelectron spectroscopy and secondary ion mass spectroscopy revealed a copper concentration on the order of five atomic percent throughout the HfOx film. In addition to the Cu doped HfOx, a thin layer (20 nm) of CuxO is present at the surface. This surface layer is believed to have formed during the ALD process, and greatly complicates the analysis of the switching mechanism. The resistive memory structures fabricated from the ALD HfOx exhibited non-polar resistive switching, independent of the top metal electrode (Ni, Pt, Al, Au). Resistive switching current voltage (I-V) curves were analyzed using Schottky emission and ionic hopping models to gain insight into the physical mechanisms underpinning the device behavior. During the forming process it was determined that, at voltages in excess of 2.5 V, an ionic hopping model is in good agreement with the I-V data. The extracted ion hopping distance similar to 4 angstrom was within the range of interatomic spacing of HfO2 during the forming process consistent with ionic motion of Cu2+ ions. Lastly the on state I-V data was dominated at larger voltages by Schottky emission with an estimated barrier height of similar to 0.5 eV and a refractive index of 2.59. The consequence of the Schottky emission analysis indicates the on state resistance to be a product of a Pt/Cu2O/Cu filament(s)/Cu2O/Cu structure. (C) 2014 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available