Ring opening; Polymerization; PBT; DSC; Crystallization; Melting
Funding
- Regione Puglia (Italy)
Ask authors/readers for more resources
Differential scanning calorimetry was used to study the thermal characteristics and morphological structure of species produced during the ring opening polymerization of cyclic butylene terephthalate (CBT). Thermal programs consisting of a first ramp heating scan and an isothermal step, followed by cooling and a second ramp heating step, were used to study the effects of thermal history, catalyst (butyl chlorotin dihydroxide) at concentrations between 0.1 and 1.3% (w/w), and the presence of a layered silicate nanofiller (montmorillonite at 4.0%, w/w) on the structure of the resulting polymer (poly(butylene terephthalate), pCBT). Wide angle X-ray diffraction was used to monitor the degree of exfoliation of the nanocomposites. It was found that pCBT is formed in the amorphous state, and crystallizes during the heating step or during the isothermal step at temperatures lower than the equilibrium melting temperature of the polymer(T-m(0)). When premixed with the nanofiller, irrespective of whether this was previously intercalated with a tallow surfactant or used in its pristine form, polymerization took place at higher temperatures and most of the crystallization was found to occur during the cooling stage. In those cases where crystallization took place during either the first heating scan, or during a prolonged isothermal step below the T-m(0), of the polymer, the resulting crystals were found to have a higher lamellar thickness, as compared with the same polymer crystallized from the melt during the cooling step from temperatures above the polymer T-m(0). (C) 2009 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available