SURFACE & COATINGS TECHNOLOGY
Volume 223, Issue -, Pages 11-16Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2013.02.019
Keywords
Hydrogen-free DLC; Thin films; Biased target ion beam deposition; Bias voltage; Bonding sp(3)
Funding
- Canada Research Chair Program
- Natural Sciences and Engineering Research Council of Canada (NSERC)
Ask authors/readers for more resources
Biased target ion beam deposition (BTIBD) was firstly used to synthesize hydrogen free diamond-like carbon (DLC) thin films. The structure and properties of the synthesized films were characterized by atomic force microscopy (AFM), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), nanoindentation, and ball-on-disk testing. The effect of target bias voltage, ranging from - 200 to - 1000 V, on the structure and properties of the films was investigated. The results show that the sp(3) bonding content increases from 20% to 60%, the root-mean squared (RMS) roughness decreases from 0.2 nm to 0.05 nm, the coefficient of friction (COF) decreases from 03 to 0.06, the hardness increases from 4.5 GPa to 15 GPa, and the Young's modulus increases from 65 GPa to 170 GPa with increasing the absolute value of target bias voltage from 200 V to 800 V. However, when the target bias voltage further increased to - 1000 V, the sp(3) bonding content decreases to 44%, RMS roughness increases to 0.09 nm, COF raises to 0.11, hardness decreases to 12.9 GPa and Young's modulus is lowered to 150 GPa. It has been found that the higher the fraction of sp(3) bonds, the lower the surface roughness and friction coefficient, and the higher the hardness and Young's modulus. (C) 2013 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available