Journal
SURFACE & COATINGS TECHNOLOGY
Volume 202, Issue 14, Pages 3239-3245Publisher
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2007.11.028
Keywords
multilayer; metallic glass; mechanical properties; shear bands
Ask authors/readers for more resources
The mechanical properties of Co79Zr13Nb8/Cr multilayers were investigated using nanoindentation. The hardness is higher than the average value calculated by rule-of-mixture. The hardness and the resistance to plastic deformation characterized by the ratio of H-3/E-2 Vary Similarly With periodicity (Lambda). They all arrive to the maximum at Lambda= 8 nm and decrease subsequently when the A increases. The hardness dependence on the A is fitted by Hall-Petch relation. The fitted index n is much lower than the normal value (similar to 0.5) in many crystalline multilayers. The mutual restriction of shear band and dislocation in amorphous/crystalline structure, which is named structure barrier strengthening, should be main mechanism for the hardness enhancement. The SEM study of indents shows that the shear bands are distorted significantly at the smaller Lambda (4 nm) and disappear at the larger Lambda (> 20 nm). This morphology variation implies a potential improvement of plasticity caused by the restriction effect of the Cr crystalline layers on the shear bands propagation. (c) 2007 Elsevier B.V. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available