Journal
RSC ADVANCES
Volume 5, Issue 20, Pages 15515-15523Publisher
ROYAL SOC CHEMISTRY
DOI: 10.1039/c4ra14354j
Keywords
-
Categories
Funding
- Union Funds of the National Natural Science Foundation of China [U1034003]
- Key Projects of the Natural Science Foundation of Heilongjiang Province [B201105]
- Special Funds for Investment of Sci-tech Innovation of Harbin [2012RFXXG102]
Ask authors/readers for more resources
1D highly crystalline mesoporous In2O3 nanowires (INWs) coated by an amorphous silica (HCMIAS) ultrathin surface layer were successfully fabricated using SBA-16 as a hard template. Various techniques, including XRD, SEM, TEM and X-ray photoelectron spectroscopy (XPS), were employed for material characterization. All the results demonstrated that the obtained INW-2 sample, which contained 15 at% SiO2 and 85 at% In2O3 in 0.2 M In(NO3)(3) solution, displayed high crystallinity with a rough surface coating layer of SiO2 in the atomic scale. The domain diameter of INW-2 was approximately 4-8 nm with the pore size of 3-5 nm. The NOx sensing properties of the INW-2 sensor exhibited an ultra-high response and selectivity with the low detection limit of 0.97 ppm and high response of 115.6 to 97.0 ppm NOx at RT. The excellent gas sensing property of the 1D morphology with amorphous silica was associated with its higher surface area and space-charge layer, which induced highly effective surface interactions between the target gas molecules and the surface active sites. Moreover, the synergetic and electronic effect on INW-2 favored the effective adsorption of NOx on the surface. All the factors considered had evident beneficial effects on enhancing the gas sensing performance of the sensor.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available