Journal
RADIATION PHYSICS AND CHEMISTRY
Volume 81, Issue 9, Pages 1341-1344Publisher
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.radphyschem.2012.01.047
Keywords
Radiation induced grafting; Styrene; Poly(vinylidene fluoride)
Ask authors/readers for more resources
Radiation-induced grafting of styrene into poly(vinylidene fluoride) (PVDF) films with 0.125 mm thickness at doses of 1 and 2.5 kGy in the presence of a styrene/N,N-dimethylformamide (DMF) solution (1:1, v/v) and at doses of 20, 40 and 80 kGy in presence of a styrene/toluene solution (1:1, v/v) at dose rate of 5 kGy h(-1) was carried out by the simultaneous method under nitrogen atmosphere and room temperature, using gamma rays from a Co-60. The films were characterized before and after modification by calculated grafting yield (GY %), infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), differential scanning calorimetry (DSC) and thermogravimetry (TG/DTG). GY results shows that grafting increases with dose, and the grafting of styrene was confirm by FT-IR due to the new characteristic peaks and by the TG and DSC attributed to changes in thermal behavior of the grafted material. Results showed that the system allows the controlled grafting of styrene into PVDF using gamma rays at doses as low as 1 kGy in DMF. (C) 2012 Elsevier Ltd. All rights reserved.
Authors
I am an author on this paper
Click your name to claim this paper and add it to your profile.
Reviews
Recommended
No Data Available