Effect of matrix viscosity on the extent of exfoliation in EVA/organoclay nanocomposites

The influence of matrix viscosity and polarity on ethylene-vinyl acetate copolymer (EVA) nanocomposites was studied. Five different EVA grades, with different melt flow indexes (MFIs) and/or vinyl acetate (VA) contents, were mixed with two montmorillonite (MMT) nanoclays: pristine and modified with a polar surfactant, producing 75/25 w/w% masterbatches which were subsequently diluted in the EVA matrix to obtain 5 wt% MMT nanocomposites. Although the same VA content, WAX5 results, rheological measurements and TEM analysis showed that the lower the EVA viscosity, the greater the tendency to obtain exfoliated and well dispersed nanocomposites with the organically modified clay. On the other hand, the high viscosity EVA nanocomposites showed that the (001) organoclay diffraction peak was shifted to higher values of 20, suggesting lamellae collapsing. TGA and FTIR measurements were used to probe the thermal degradation of organoclay; furthermore, it was not possible to identify, by the techniques used, any reaction between the VA groups and hydroxyl surfactant groups. Thus, it was inferred that the organic surfactant was removed (or ejected) from the clay galleries as a consequence of huge shear tensions developed during processing of the masterbatches/nanocomposites with high viscosity EVA matrices. Copyright (C) 2009 John Wiley & Sons, Ltd.