Synthesis and analysis of injection-molded nanocomposites of recycled high-density polyethylene incorporated with graphene nanoflakes

Journal

POLYMER COMPOSITES
Volume 36, Issue 9, Pages 1565-1573

Publisher

WILEY
DOI: 10.1002/pc.23063

Keywords

-

Funding

  1. Department of Energy [DE-EE0004167]
  2. Wichita State University

Ask authors/readers for more resources

Recycled high-density polyethylene (HDPE) was incorporated with graphene nanoflakes in a solvent at different concentrations (0, 1, 2, 4, and 8 wt%), and then the mechanical, thermal, electrical, and surface hydrophobic properties of the resultant nanocomposites were determined using universal tensile testing, thermal comparative, capacitance bridge, and goniometer techniques, respectively. The test results revealed that the mechanical, thermal, and dielectric properties of the polymer matrix nanocomposites were increased as a function of graphene concentrations, whereas the surface hydrophobic values were slightly increased at lower concentrations and then reduced at higher concentrations. These improvements occur mainly because of the excellent properties of graphene nanoflakes, such as tensile strength (150 GPa), Young's modulus (1.0 TPa), thermal conductivity (4,840-5,300 W/m K), electrical conductivity (1.3 x 10(6) S/cm), electrical current density (10(13) A/cm(2)), surface hydrophobicity (>120 degrees), and surface smoothness/roughness (<1 nm). The worldwide consumption of polymeric products has been drastically growing, and consequently polymeric waste materials have been rising up, as well. Although the plastic recycling and reprocessing rates are considerably high, physical properties and economical values of the recycled plastics are significantly low, limiting the reuse of recycled plastics in many industrial applications. As a result, this study provides a detailed explanation of how to improve recycled plastics into highly valued new products for applications in various industries, such as transportation, energy, electronic, construction, and so forth. POLYM. COMPOS., 36:1565-1573, 2015. (c) 2014 Society of Plastics Engineers

Authors

I am an author on this paper
Click your name to claim this paper and add it to your profile.

Reviews

Primary Rating

4.7
Not enough ratings

Secondary Ratings

Novelty
-
Significance
-
Scientific rigor
-
Rate this paper

Recommended

No Data Available
No Data Available