Mechanical Properties of Poly Lactic Acid Composite Films Reinforced With Wet Milled Jute Nanofibers

In the present study, waste jute fibers generated in textile industries, were wet pulverized to the scale of nanofibers of 50 nm diameter using high energy planetary ball milling for 3 h. The presence of water during wet pulverization found to reduce the rising temperature of mill, which prevented sticking of nanofibers on the mill wall and resulted in unimodal size distribution. In the subsequent stage, 1, 5, and 10 wt% of jute nanofibers were incorporated in poly(lactic acid) (PLA) matrix to prepare nanocomposite films by solvent casting. The reinforcement of nanofibers was investigated from the improvements in mechanical properties based on tensile tests, dynamic mechanical analysis, and differential scanning calorimetry. The maximum improvement was observed in case of 5 wt% nanocomposite film where initial modulus and tensile strength increased by 217.30% and 170.59%, respectively as compared to neat PLA film. These improvements are attributed to the increased interaction between nanofibers and matrix as well as to the increased crystallinity of PLA in composites. The improvements in load bearing capacity of nanocomposite films were significant at 60 degrees C than 35 degrees C, which showed ability of jute nanofibers to improve the softening temperature of PLA matrix. In the end, experimental results of Young's modulus were compared with predicted modulus of mechanical models. A good level of agreement was observed up to 5 wt% loading of jute nanofibers. POLYM. COMPOS., 34:2133-2141, 2013. (c) 2013 Society of Plastics Engineers